FPU Industrial 501 Extra HD

NDG FPU 501 Extra HD Industrial

Colour: Clear
Finish: Super Glossy
Flash Point: 20C
Reduction Solvent: T-4
Clean-Up Solvent: T-4
Volume Solids %: Approx. 39%
Pot Life: 4 – 6 hrs. depending on an ambient temperature

Thinning: Can be thinned to desired viscosity using Butyl Acetate
Shelf Life: Up to 12 months as long as the sealed containers are kept under cover in a dry place under normal temperature conditions. Recommended DFT/Coat: 40 – 50 microns

Theoretical Covering Capacity (TCC): 10.00m2/litre @ 40 microns DFT 7.80m2/litre @ 50 microns DFT

No. of Coats: 2
Drying Time: 15C – 30C
Surface Dry: 1 – 2 hours
Hard Dry: 16 hours
To Re-Coat: Min. overnight – max 7 days To Full Cure: 6 – 7 days
Over Coating Interval: Overnight

Performance Data

• Abrasion Resistance: Excellent Adhesion: Excellent Flexibility: Excellent
• Impact Resistance: Excellent Humidity Resistance: Excellent
  Chemical Resistance: Excellent
• Water: Excellent Alkalies: Excellent Inorganic Acids: Good
• Organic Acids: Good
• Good Organic Solvents: Good

Surface Preparation Direction for Use

Previously Painted, Powder-coated or Primed Surfaces:
The surface to be coated must be dimensionally stable, dry, clean and free of oil, grease, release agents, curing compounds and other foreign materials.
All bare areas must be primed with suitable primer:
New steel must be grit blasted & glossy surfaces should be roughened before re-coating. If any old paint that is peeling, flaking, cracking, blistering or lifting must be removed. Scuff sand glossy areas and aged epoxy coatings. All edges of the old coating must be feathered down to remove sharp edge.

Bare Steel:

All surfaces shall be free of loose rust, mill-scale and contaminants such as oil, grease, dirt and salts. Before any surface preparation is attempted, oil and grease must be removed by employing a suitable solvent cleaning.
Use commercial Blast cleaning to remove mill-scale, rust and other contaminants and leave a roughened surface.

Concrete and Masonry:

Remove all loose particles, oil, grease, form release agents and any other contaminants. New concrete and masonry must be allowed to cure for a minimum of 30 days.
Before painting, roughen the surface by abrasive blasting, acid etching or scarifying.

Special Notes

• Thinner (Butyl Acetate) consumption may vary depending upon site conditions.
• Practical covering capacity depends on application techniques, ambient conditions, wastage, surface conditions etc.

Mixing Instructions

Thin according to requirements using Butyl Acetate up to ratio 1:1
If the settling is observed in the base, loosen the settled material with help of hand stirrer followed by power driven stirrer. For best results, use a spiral mixing blade at variable speed (400 – 600 rpm). Place the spiral mixing blade at the bottom of the container before turning on the mixer.

This will help to avoid inducting air into the material. Inducted air will cause “bubbles” in the coating when applied. Gently move the mixer head up to the surface while running.

This product has workable pot life 6 hours at ambient temperature.

Applying the material immediately after the 30 minutes induction time will provide best results.

Note: Higher air & mixture temperatures will decrease the pot life and working time.

Application Information:

Generally this paint is best applied by spray. Due to the rapid dry of this coating, only small areas may be coated by brush, applicator pad or roller.
Care must be taken to achieve the specified wet and dry film thicknesses. Uniform, even coats must be obtained.

Large horizontal surfaces should be spray applied, however roller application can be performed.

Application Methods:

• Spray – Use airless spray or conventional spray.
• Brush – Recommended for stripe coating and small areas, care must be taken to achieve the desired results.
• Roller – May be used for small areas but not recommended for first primer coat, however when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

NDG FPU 501 Extra Heavy Duty Industrial Coating Test Results

Adhesion ASTM D 3359 Cross Cut Tape test – Excellent

Abrasion Resistance ASTM D 4060 C 17 Wheels, 1000 gm load, 1000 cycles 50 mg

Impact Resistance ASTM D 2794 Gardiner Impact, 7 Day Air Dry at 25 C – Excellent Flexibility ASTM D 522 Conical Mandrel Apparatus – Excellent
Chemical Resistance 5% NaOH – No Effect
24hr Covered Watch 5% H2SO4 – No Effect

Glass Spot Test 100% Xylene – No Effect
100% Mineral Spirits – No Effect
Hardness ASTM D 3363 Pencil 7 Day Cure 6H Exterior Durability ASTM G 53

Accelerated aging via exposure to Fluorescent, Ultraviolet and Condensation – Excellent Salt Fog Resistance
ASTM B 117 Salt Spray Test 400hrs – No Effect
Immersion Ambient 1500hrs – No Effect

Graffiti Resistance Crayon, Ink Pen, Marker, Shoe Polish – Excellent Hot Water Immersion 8C 800hrs – No Effect